SmCo Se Tun a npè Pẹlu SmCo se, irin, SmCo Yẹ Magnet, SmCo Yẹ se Iron Ati Rare-Earth koluboti Yẹ Magnet. O ni A Irú Of elo Made Lati Raw Earth Irin Samarium Ati koluboti Ati Produced Nipa Lẹhin A Serial Of Process Burdening, yo, milling, titẹ Ati Sintering .O & rsquo: S Tun A to gaju imuše ni, Low otutu olùsọdipúpọ Yẹ Magnet Pẹlu oniwe-High Ṣiṣẹ otutu & Mdash; 350 ìyí Centigrade. Nigba ti Nṣiṣẹ Above 180 ìyí Centigrade, Awọn oniwe-pọju Energy ọja BH Ati Dada otutu o wa Superior ju NdFeB se elo. O Needn & rsquo: T Lati Ki Bo Nitori O Se Soro Lati Ki eroded Ati oxidized. SmCo Magnet ni opolopo lo Ni Space ibere, National olugbeja Ati Military, Makirowefu Ohun elo, Communication, Medical ẹrọ, Motors, Instruments, Opolopo Magnetism Ntan Devices, sensọ, se isise, se Lifter Ati Nítorí On.

ọja Image

15331172725275846

ti ara Abuda

Apa kan ara ini Of Sintering SmCo oofa
paramita Name Unit SmCo1: 5 SmCo2: 17
iwuwo G / Cm3 8.3 8.4
Curie otutu K 1000 1100
Vickers líle MPA 450-500 550-600
compressing Okun MPA 1000 800
itanna Resistivity Ω.Cm 5 ~ 6 & Times; 10-5 8 ~ 9 & Times; 10-5
atunse Okun Mpa 150-180 130-150
nínàá Okun Mpa 400 350
Hot alafisodipupo fun Imugboroosi (10 -6 / ℃) ∥6⊥12 ∥6⊥11

Akiyesi: Awon Above Specific NỌMBA Help To Kan, Ko To Jẹ The Adajo sáyẹńsì

15331298979058714

Akiyesi: Agglutinates Gbogbo The Samarium koluboti 2: 17 Ọpọlọpọ lowers Nilo The lopolopo Magnetizing Field Se elo ara HCj Iye 2-3 Times

 

Ti iwa awọn afiwera Of Yẹ se elo
ohun elo (BH) Max IHc br TC (Ṣiṣẹ otutu) Max Anti-Causticity
SmCo1: 5 16-25 15-25 -0,05 200-250 ti o dara
SmCo2: 17 22-30 6-30 -0,03 300-350 ti o dara
NdFeB 26-52 12-30 -0,11 80-200 buburu
Ferrite Magnet 3-4.5 3-4.5 -0,19 200-300 ti o dara
AINiCo 5-10 1-1.8 -0,03 450-500 o tayọ

Awọn Ile ká Technology Ati Anfani:

1, NGYC Ni Ọpọlọpọ ti ni ilọsiwaju Production Ati ayewo Equipment .We o wa Professional SmCo oofa Idawọlẹ Eyi ti o ni Largest asekale Ati wu Ni China.
2, wa Company le so Max. Block 120mm & Times; 120mm & Times; 100mm Pẹlu Full Magnetization.
3, NGYC le Pese ipele Production Fun High ite YXG-32 Pẹlu BH & Ge; 29MGOe.
4, NGYC le fi ranse Ibi Of SmCo oofa Pẹlu Ga Ibùso Performance Ati High HK (HK & Ge; 18KOe).
5, NGYC le so SmCo oofa Nipasẹ asiali Pẹlu Ọpọlọpọ awọn ọpá.
Strong Style = "awọ: # 0e5f91;"> bi han:

15331316853546049_e

6, wa Company le Pese The oofa Pẹlu iyapa Kere ju 2 & Deg; Laarin darí Ipo Ati se Ipo.
 As Shown:

15331317057106443_e

anfani ti advices

(1) Sintered SmCo Yẹ se elo Ni The kikọ Of Brittleness, Ew Of The Ductility. Ki It Isn & rsquo: T dara fun Lilo Bi igbekale Apá Nigba ti Jije Apẹrẹ. Awọn ara pato Of SmCo (1: 5) Ṣe Dara ju SmCo (2:17) & rsquo: S Nitori SmCo (1: 5) Ṣe Easy To Machine Nigba ti SmCo (2:17) Ṣe Die brittle. SmCo Yẹ Magnet Magnetized Gbọdọ wa ni ti gbe Up Fara Nigba Awọn ilana Of Nto, Etanje Ironware To Dena absorbing tosi Ati Awọn oofa bu Pa, Tabi meji Ege Of se Irons Fa bibajẹ yorisi ni absorbing Papo, Yato si, O Yoo Ani mu Ara-Hurt
( 2) Sintered SmCo Yẹ se elo Ṣe Ṣe Diẹ ninu awọn Iwonba ijamba Ni Awọn ilana ti producing, Iṣakojọpọ Ati fi, Nítorí náà, Nibẹ ni le Jẹ Ni Diẹ ninu awọn wiwo flaw wáyé A bit Kekere Horn. Sibẹsibẹ, O yoo & rsquo: T ba oniwe se pato, Awọn oniwe-iduroṣinṣin Ati oniwe-Anti-degenerated se Agbara Bi Long Bi oniwe-flaw Doesn & rsquo: T Kàn Deede Ikole Tabi iṣẹ.
(3) ibara Ta Béèrè Non-Magnetized SmCo Yẹ Magnet Gbọdọ Jẹ acquaint Pẹlu Self-Magnet awọn ẹrọ Fun The Purpose Of Patapata satiate Ati Magnetize ọja wa Tabi koodu.
(4) Ti o ba ti The Apẹrẹ Products Ṣe awọn Ni ekan alkali Tabi Buru to agbegbe, Wa Company le Pese ọja Of Zn, Ni, Gold Tabi wreath atẹgun Palara. A Lero Gan graceful Fun rẹ Awọn ohun elo. Kaabo To Fax Tabi Ṣe Email Ijumọsọrọ. A ni o wa dùn Lati Ran O Pẹlu Gbogbo Isoro Of The imuposi. A Gbogbo Work Lile gbiyaju Lati Pese O SmCo Yẹ se elo Pẹlu Top-didara Ati Low-Price.